G85-A2可程式复合盐雾试验箱满足G85–09Standard Practice for Modified Salt Spray (Fog) Testing中A2测试标准，实现盐雾、强制干燥、高湿三个过程的交替循环测试！

可程式复合盐雾试验是一种综合性盐雾试验，将产品在盐雾、强制干燥、湿热三种环境条件下交替转换，来考核整机产品的电性能和机械性能有无变化。

G85-A2复合盐雾试验箱的测试条件：

A3.1 Salt Solution:

A3.1.1 Use a synthetic sea salt solution made in accordance with 6.2 with the addition of 10 mL of glacial acetic acid perlitre of solution.

A3.1.2 Adjust the pH of the salt solution between 2.8 and 3.0.

A3.2 Conditions in Saturator Tower—Make sure the tem-perature in the saturator tower (bubble tower) is 47 6 1°C(1176 2°F) if cabinet temperature is 35°C (95°F); and 57 61°C (135 6 2°F) if cabinet temperature is 49°C (120°F).

A3.3 Conditions in Salt Spray Chamber:

A3.3.1 Temperature—The temperature in the exposure zoneof the salt spray chamber may vary to suit the material beingtested. The specifications that cover the material or productbeing tested define the temperature or the temperature may bemutually agreed upon between the purchaser and the seller. See Note A3.1 for recommended exposure zone temperatures forsome materials.

NOTE A3.1—This test is particularly applicable to production control ofexfoliation-resistant heat treatments for the 2000, 5000, and 7000-seriesaluminum alloys. 4 It is also applicable to developmental studies of varyingheat treatment parameters to determine effect on corrosion behavior. Forthis purpose, a temperature of 49°C (120°F) is recommended for theexposure zone. For testing organic coatings on various metallic substrates,an exposure zone temperature of 24 to 35°C (75 to 95°F) may be used since temperatures in excess of 35°C frequently result in paint blistering.

A3.3.2 Humidity—Although the humidity limits for opti-mum test conditions have not been determined, results of aninterlaboratory testing program indicate that it is necessary to operate under wet bottom conditions (that is, an inch or so of water should always be present in the bottom of the box). This ensures that the interior of the box does not become dry, a condition that will decrease the corrosion rate.

A3.3.3 Cabinet—Equip the cabinet with a timing device that can be used for the following cycle: 30-min spray followed by 90-min soak at above 98 % relative humidity.

翻译成中文，测试条件如下：

1、试验室温度：49度；

2、饱和桶温度：57度；

3、盐水浓度：5%，PH值要求2.8-3.0之间；

4、首先进行0.75小时的盐雾试验，然后2小时内吹入干燥的空气；

5、将测试产品静置于高湿环境保持3.25小时，湿度要求从65%最后上升到95%；

6、上述3个过程总计6小时，然后循环多次进行。

G85-A2复合盐雾试验箱参数：

1、试验室温度范围:+35℃～+60 ℃

2、相对湿度: 30%～98%（±3%）

3、饱和桶温度: 47℃～70 ℃

4、温度均匀度: ≤±1℃

5、温度波动度: ≤±2℃

6、试验时间:0～999H、M可调

7、沉降量:1-2ml/80cm2/h

9、在触摸屏控制器内可编程喷雾、干燥、潮湿过程并设定循环次数

9、除雾方式:通过空气挤压排雾

10、电压：380v/50HZ，功率:6.5KW

11、重量约:400KG

12、使用环境温度:10℃～35 ℃

13、使用环境湿度：≤85%

14、 复合盐雾试验箱的包装满足QB/TST008-2001要求的运输包装箱

G85-A2可程式复合盐雾试验箱技术规格：

型号（CM）	KD-108-S	KD-270-S		KD-412-S		KD-663-S	KD-1080-S
工作室尺寸	456040		609050	7511050		8513060	9020060
外型尺寸	70120110		95150120	110170125		115210155	125280160
功率	1.3(kw)		1.5(kw)	4.0(kw)		5.0(kw)	6.5(kw)
温度范围	＋10℃～60℃
湿度范围	30～98%
温度均匀度	±2℃
温度波动度	±0.5℃
盐雾沉降量	1～2ml/80cm².h
喷雾方式	连续、周期任选
控制器	进口可编程触摸式液晶中英文对话式显示.微电脑集成控制器
温度传感器	铂金电阻.PT100Ω/MV
加热系统	全独立系统，镍铬合金电加热式加热器
喷雾系统	塔式喷雾装置加无结晶喷嘴（雾粒更细且分布均匀）
喷雾时间	1～9999（H、M、S）且周期可调
盐液收集	配标准漏斗和标准计量筒
盐液过滤	吸液管处装配水质过滤器（防止喷嘴堵塞终止试验）
盐液预热	盐液温度与箱内温度均衡（不致盐液温度过低影响试验温度）
标准配置	圆棒、V型样品架各1付、喷嘴2只、漏斗，计量筒2套
安全保护	漏电、短路、超温、缺水、试验结束、过电流保护
电源电压	AC220V±10％ 50Hz				AC380V±10％ 50Hz
使用环境温度	5℃～＋30℃ ≤85％R.H
密封	采用水密封结构，无盐雾溢出
注：可单独做湿热试验或盐雾试验,可根据用户需求定制大型步入式复合盐雾试验室